摘要 : The effects of Nb addition on microstructures and formability in Si-Al-Mn TRIP cold-rolled steels were investigated. These steels were intercritical annealed at 770℃ for 5 min, and isothermally treated at 400 ℃ for 3 min. Micros... 展开 The effects of Nb addition on microstructures and formability in Si-Al-Mn TRIP cold-rolled steels were investigated. These steels were intercritical annealed at 770℃ for 5 min, and isothermally treated at 400 ℃ for 3 min. Microstructural observation, tensile tests and forming limit diagram (FLD) tests were conducted, and the changes of retained austenite volume fraction as a function of tensile strain were measured by using an X-ray diffractometer. The results showed that Nb addition makes grain size refined, the volume fraction of ferrite increase and that of bainite decrease, however, obviously it does not affect the volume fraction and carbon content of retained austenite. The Nb addition increased the stability of retained austenite owing to grain refinement. With Nb addition, increase in strength, ductility, strain hardening exponent and formability could be achieved simultaneously. These findings indicate that Nb addition can be a new direction of microalloying design for the low carbon TRIP steels with excellent formability and high stability of retained austenite. 收起