摘要 : In the present study, the modified high Ti-bearing blast furnace slag was prepared by adding 2.5% B2O3. The precipitation behavior of anosovite was studied by the procedure which was pre-melted at 1360 degrees C for 20 min, cooled... 展开 In the present study, the modified high Ti-bearing blast furnace slag was prepared by adding 2.5% B2O3. The precipitation behavior of anosovite was studied by the procedure which was pre-melted at 1360 degrees C for 20 min, cooled to 1260 degrees C at the rates of 0.25-4.0 degrees C/min, and then quenched into the ice water after duration for 60-240 min at 1260 degrees C. Phase assemblage and composition of the slag quenched from high temperature was determined by the electron probe X-ray microanalysis (EPMA). The micrographs of slags were obtained by optical microscope and the dimension data of anosovite was collected by ImageJ software. The theory of Crystal Size Distribution (CSD) was adopted for data processing and crystallization kinetics study. The results showed that B2O3 distributed only in liquid phase of the slag and anosovite was the host mineral precipitated from the current modified high Ti-bearing blast furnace slag. The decrease of cooling temperature and prolonging holding time were both beneficial to grain coarsening of anosovite. The growth rate (G) and nucleation rate (J) of anosovite phase were similar and they both decreased exponentially with holding time. 收起