《Journal of Non-Crystalline Solids: A Journal Devoted to Oxide, Halide, Chalcogenide and Metallic Glasses, Amorphous Semiconductors, Non-Crystalline Films, Glass-Ceramics and Glassy Composites》 2016年452卷
摘要
:
Glasses based on the system of Y2O3-BaO-Nb2O5-B2O3, corresponding to the pseudo-binary 64Ba(1 - x)Y(2x/3)Nb(2)O(6)-B2O3 with x = 0.1-0.5, were prepared, and their thermal properties, electronic polarizabilities, optical basicities...
展开
Glasses based on the system of Y2O3-BaO-Nb2O5-B2O3, corresponding to the pseudo-binary 64Ba(1 - x)Y(2x/3)Nb(2)O(6)-B2O3 with x = 0.1-0.5, were prepared, and their thermal properties, electronic polarizabilities, optical basicities, and crystallization behavior were clarified. The glasses showed the glass transition temperature of 602-610 degrees C, crystallization peak temperature of 686-676 degrees C, and refractive index of 1.967-2.007. All the glasses showed the bulk crystallization behavior, providing Ba1 - xY2x/3Nb2O6 nanocrystals with a tetragonal tungsten bronze structure. It was found from high resolution transmission electron microscope observations that the morphology of Ba1 - xY2x/3Nb2O6 nanocrystals is ellipsoidal and their average particle size is in the range of 20-40 nm. The glass-ceramics with Ba1 - xY2x/3Nb2O6 nanocrystals showed high dielectric constants (frequency: 1 kHz) of similar to 90 at room temperature and a ferroelectric nature. Highly oriented Ba1 - xY2x/3Nb2O6 crystal lines were patterned by laser (continuous wave Yb:YVO4 fiber laser with a wavelength of 1080 nm) irradiation with the condition of a laser power of 1.9 W and a laser scanning speed of 4 pm/s and with the laser focal position of 20 mu m beneath from the surface in 2NiO-1.1Y(2)O(3)-29.8BaO-33.1Nb(2)O(5)-36B(2)O(3) glass. (C) 2016 Elsevier B.V. All rights reserved.
收起