摘要 : The diamagnetic zinc oxide (ZnO) nano-crystallites were synthesized via the sol-gel method. The X-ray diffraction (XRD) and field emission scanning electron microscope (FESEM) were used for structural characterization. The XRD pat... 展开 The diamagnetic zinc oxide (ZnO) nano-crystallites were synthesized via the sol-gel method. The X-ray diffraction (XRD) and field emission scanning electron microscope (FESEM) were used for structural characterization. The XRD pattern demonstrates that the ZnO nanoparticles (NPs) have a wurtzite structure with an average crystallite size of similar to 20 nm. TheFESEM and EDAX (energy-dispersive x-ray analysis) confirm the particles are in granular, spherical, and rod-like mixed-phase. The absorption spectra show a red shift and observed bandgap energy of about 3.17 eV, which might attribute because of the oxygen vacancies. Further, photoluminescence (PL) exhibits dual peaks at wavelengths 430 and 550 nm, which maybe due to defects induced at the surface of the NPs. The vibrating sample magnetometer (VSM) study demonstrates the diamagnetic behavior of zinc oxide nanoparticles at 300 K. The photocatalytic effectiveness of the ZnO NPs was examined by decomposing a congo red (CR) dye as an organic water pollutant under UV irradiation. The leading absorption peak of CR dye decreases with the UV irradiation time. The complete decolorization of the CR dye was observed after 150 min with the reaction rate constant of 0.018 min(-1). 收起