摘要 : This study was conducted to simulate a pin-type thin film solar cell by integrating nc-Si:H as p-window and buffer layers. The structures proposed to investigated are ITO/(p)nc-Si:H/((i)a-Si:H/(n)a-Si:H/Ag and ITO/(p)nc-Si:H/(p')n... 展开 This study was conducted to simulate a pin-type thin film solar cell by integrating nc-Si:H as p-window and buffer layers. The structures proposed to investigated are ITO/(p)nc-Si:H/((i)a-Si:H/(n)a-Si:H/Ag and ITO/(p)nc-Si:H/(p')nc-Si:H(buff)/(i)a-Si:H/(n)a-Si:H/Ag simulated with the AFORS-HET simulator. In an effort to improve the electrical and optical properties of the heterojunction solar cell, the dopant concentration for the p-window and n-layers, the absorber bandgap, and the absorber thickness were optimized. The result showed that the E-ff of p-p'-i-n is 9.60% (V-OC = 936.6 mV, J(SC) = 13.86 mA/cm(2), FF = 0.738) were obtained when values of Na, Nd, absorber bandgap, and absorber thickness parameters are 1.0 x 10(17) particles/cm(3), 1.0 x 10(19) particles/cm(3), 1.80 eV, and 600 nm, respectively. 收起