摘要 : We have prepared a large number of crystals of cuprous oxide (Cu2O) by various procedures. Photoluminescence spectra of these crystals were studied to examine the concentration of defects, especially copper vacancy V-Cu to seek fa... 展开 We have prepared a large number of crystals of cuprous oxide (Cu2O) by various procedures. Photoluminescence spectra of these crystals were studied to examine the concentration of defects, especially copper vacancy V-Cu to seek favourable conditions for growing Cu2O crystal. High-quality single crystals of Cu2O were prepared by the floating-zone melting method in air. Several synthetic crystals (specimens FA, FZ and GZ) and also a natural crystal were studied by X-ray analysis, inductively coupled plasma spectroscopy analysis, optical absorption, photoluminescence, photoconductivity and cyclotron resonance absorption, photoluminescence, photoconductivity and cyclotron resonance absorption to characterize their optical and electrical qualities. The best values of mobility and scattering time of photocarriers at T = 4.2 K are estimated to be mu(h) approximate to 1.8 x 10(5) cm(2) V-1 s(-1) and tau(h) approximate to 60 ps for positive holes, and mu. approximate to 1.3 x 10(5) cm(2) V-1 s(-1) and tau. approximate to 70 ps for electrons in Cu2O. Further, we report preliminary experimental results on transport property of crystals also of cupric oxide (CuO) purified by the floating-zone melting method. (C) 1998 Kluwer Academic Publishers. [References: 50] 收起