《Journal of Non-Crystalline Solids: A Journal Devoted to Oxide, Halide, Chalcogenide and Metallic Glasses, Amorphous Semiconductors, Non-Crystalline Films, Glass-Ceramics and Glassy Composites》 2008年354卷42/44期
摘要
:
The presence of Lewis and Bronsted acid sites in calcined mixed oxides 10% V2O5/SiO2, 10% V2O5/TiO2, and 10% V2O5/Al2O3 obtained by sol-gel method was determined through infrared spectroscopy using pyridine as a molecular probe. T...
展开
The presence of Lewis and Bronsted acid sites in calcined mixed oxides 10% V2O5/SiO2, 10% V2O5/TiO2, and 10% V2O5/Al2O3 obtained by sol-gel method was determined through infrared spectroscopy using pyridine as a molecular probe. Texturally, they are formed by mesopores and present high specific surface area and controlled porosity. Scanning electron microscopy revealed that vanadium is homogeneously distributed in the materials. The infrared spectra of samples submitted to different temperatures after the absorbance of pyridine were obtained. The existence of active metal ions on the surface of the materials was evidenced by the presence of Lewis and Bronsted acid sites, which confers them potential catalytic properties.
收起