摘要 : Transparent solid solution crystals of Sr[CeZr]_(0.95)Yb_(0.05)O_3 were grown by the FZ-method using a Xe-arc imaging furnace to investigate proton conductivity in mixed perovskite-type oxides. It is observed that there are at lea... 展开 Transparent solid solution crystals of Sr[CeZr]_(0.95)Yb_(0.05)O_3 were grown by the FZ-method using a Xe-arc imaging furnace to investigate proton conductivity in mixed perovskite-type oxides. It is observed that there are at least five different O-H stretching vibrational modes in these solid solutions and their intensities and peak wave numbers depend on the composition of Ce and Zr. The results of electrical conductivity showed that these materials are proton conductors as well as SrCe_(0.95)Yb_(0.05)O_3 and SrZr_(0.95)Yb_(0.05)O_3. The IR-absorption intensity and the electrical conductivity have their maxima at x = 0.8 in Sr[Ce_xZr_(1-x)]_(0.95)Yb_(0.05)O_3. The Raman spectra of solid solutions suggest that the lattice distortion was changed by addition of SrZr_(0.95)Yb_(0.05)O_3 to SrCe_(0.95)Yb_(0.05)O_3. 收起