摘要: Powders (60 mu m diam) of constantan and pure copper were compressed statically into cylindrical greens (20.3 mm diam, 5.3 mm long) with a flat interface separating the two powders. A 20-mm propellant gun was used to accelerate a ... 展开 Powders (60 mu m diam) of constantan and pure copper were compressed statically into cylindrical greens (20.3 mm diam, 5.3 mm long) with a flat interface separating the two powders. A 20-mm propellant gun was used to accelerate a flyer of Lexan, copper, or aluminum, and generate in the green a shock wave with front parallel to the Cu/constantan interface. The voltages between opposite ends of the greens were measured as a function of time and for shock pressures between 1.3 and 9.4 GPa. When the shock wave arrives at the Cu/constantan interface, the voltage signal shows an abrupt increase, which lasts between 45 and 81 ns and leads to a peak temperature T/sub p/. After this, the hotter and cooler parts of the compact equilibrate and the temperature decreases to a value T/sub h/. With increasing shock pressure, T/sub h/ increases from 425 to 1215 K. The measurements of T/sub h/ are in excellent agreement with the temperatures calculated from the measured flyer velocity, the Hugoniot for copper powder, and thermodynamic data for the flyer and powders. (ERA citation 10:046740) 收起